Synthesis routes and parameters such as synthesis time, precursor molar ratio, pH, and temperature are critical for generating oxides of various sizes and morphological aspects. However, there is no information on how to prepare silver tungstate (Ag2WO4) crystals of different shapes and sizes under laboratory conditions and without using sulfating agents. In this study, we attempted to fill this gap by preparing α-Ag2WO4 crystals of various sizes and morphologies using the coprecipitation method in a 3 h interval at room temperature and without using sulfating agents. The powder X-ray diffraction analysis confirmed that all crystals had an orthorhombic structure, whereas Fourier-transform infrared spectroscopy revealed the degree of structural disorder in the bonds between the atoms in the materials. Scanning electron microscopy revealed that the α-Ag2WO4 crystals had different sizes (5.37-26.83 µm) and morphologies (tetragonal prism, rod, and cypress leave-like rod), whereas ultraviolet-visible diffuse reflectance spectroscopy analysis indicated the optical band gap energy (2.92-3.05 eV), calculated using the method proposed by Kubelka and Munk. Catalytic tests revealed that the synthesized samples with the smallest crystals (AW1) and a tetragonal prism morphology degraded dye more efficiently (apparent rate constant (k) = 5.86 × 10-3 min-1) than other samples.

Diesters of norbornene 2,3-dicarboxylic acid (NBE-(COOR)2), in which R is an alkyl group, were synthesized from one-pot synthesis method with 5-norbornene-2,3-dicarboxylic acid and methanol and ethanol. The new monomers were, respectively, the dimethyl ester NBE-(COOCH3)2 and diethyl ester NBE-(COOCH2CH3)2. Norbornene was mixed with these monomers at different proportions and copolymerized via ring-opening metathesis polymerization (ROMP) with 1st generation Grubbs' catalyst. All experiments were conducted under air atmosphere to obtain the isolated polymer. Yield results show that elongation of the R group influenced the copolymerization process. At the same co-monomer proportion, the yield decreases as a function of the R group elongation. Thermogravimetric analysis (TGA) was performed and, in all cases, more than one thermal degradation process was observed. The first process was assigned to pendent group degradation, whereas the second process was assigned to main chain degradation. These thermal processes were also influenced by different elongation of the aliphatic group of the pendent chain.

Iodide potassium incorporated on mesoporous molecular sieves (SBA-15 and MCM-41) was used as heterogeneous catalysts in the transesterification of sunflower oil under different conditions of reaction time and ratio catalyst/oil (w/w). The results have showed that the system supported in SBA-15 has been more active than the supported in MCM-41, promoting a conversion to methyl esters of 84.98%.

La-incorporated SBA-15 mesopourous molecular sieves (LaSBA-15) were directly synthesized with aim to convert ethanol to ethylene. The samples were characterized by XRD, XRF, nitrogen sorption and acidity, by thermodesorption of n-buthylamine. The results have indicated that all the samples have showed high ordered mesostructure with a large average pore size, and that the lanthanum incorporation has caused an increase in the acidity of the SBA-15. The LaSBA-15 samples have improved, with low deactivation rate, the conversion of the ethanol to water, ether, acetaldehyde and ethylene. In addition, they have increased the ethylene selectivity.